Compounds
- Elements List
- Aluminium, Al
- Antimony, Sb
- Arsenic, As
- Barium, Ba
- Berrylium, Be
- Bismuth, Bi
- Boron, B
- Cadmium, Cd
- Calcium, Ca
- Carbon, C (Graphite)
- Cerium, Ce
- Cesium, Cs
- Chromium, Cr
- Cobalt, Co
- Copper, Cu
- Dysprosium, Dy
- Erbium, Er
- Europium, Eu
- Gadolinium, Gd
- Gallium, Ga
- Germanium, Ge
- Gold, Au
- Hafnium, Hf
- Holmium, Ho
- Indium, In
- Iridium, Ir
- Iron, Fe
- Lanthanum, La
- Lead, Pb
- Lithium, Li
- Lutetium, Lu
- Magnesium, Mg
- Manganese, Mn
- Molybdenum, Mo
- Neodymium, Nd
- Nickel, Ni
- Niobium, Nb
- Palladium, Pd
- Phosphorus, P
- Platinum, Pt
- Potassium, K
- Praseodymium, Pr
- Rhenium, Re
- Rubidium, Rb
- Ruthenium, Ru
- Samarium, Sm
- Scandium, Sc
- Selenium, Se
- Silicon, Si
- Silver, Ag
- Sodium, Na
- Strontium, Sr
- Tantalum, Ta
- Tellurium, Te
- Terbium, Tb
- Thallium, Tl
- Thulium, Tm
- Tin, Sn
- Titanium, Ti
- Tungsten, W
- Vanadium, V
- Ytterbium, Yb
- Yttrium, Y
- Zinc, Zn
- Zirconium, Zr
+44 (0)1256 467055
+44 (0)1256 842929
info@testbourne.com
Aluminium, Al Compounds
Available Forms:
Evaporation Materials :
| A1-5011-M SuperVac® Aluminium Antimonide, AlSb, 6mm pieces & smaller, 99.99% pure | Evaporation Techniques | |||||
| Density g/cm3 | 4.3 | Crucible | ||||
| Melting Point °C | 1080 | Coil | ||||
| E-Beam | Boat | |||||
 | Qty in grams: | Index of Refraction @ microns | ||||
| A1-5012-M SuperVac® Aluminium Antimonide, AlSb, 6mm pieces & smaller, 99.999% pure | Evaporation Techniques | |||||
| Density g/cm3 | 4.3 | Crucible | ||||
| Melting Point °C | 1080 | Coil | ||||
| E-Beam | Boat | |||||
| Qty in grams: | Index of Refraction @ microns | ||||
| A1-5013-M SuperVac® Aluminium Fluoride, AlF3, 3-6mm pieces (pressure sintered), 99.5% pure | Evaporation Techniques | |||||
| Density g/cm3 | 3.07 | Crucible | Graphite | |||
| Melting Point °C | 1257 Sublimes | Coil | ||||
| E-Beam | Poor | Boat | Mo & W | |||
| Qty in grams: | Index of Refraction @ microns | 1.38 @ 0.55 | |||
| A1-5014-M SuperVac® Aluminium Fluoride, AlF3, 3-12mm pieces, 99.5% pure | Evaporation Techniques | |||||
| Density g/cm3 | 3.07 | Crucible | Graphite | |||
| Melting Point °C | 1257 Sublimes | Coil | ||||
| E-Beam | Poor | Boat | Mo & W | |||
| Qty in grams: | Index of Refraction @ microns | 1.38 @ 0.55 | |||
| A1-5025-M SuperVac® Aluminium Fluoride, AlF3, 6-8mm pieces, 99.995% pure | Evaporation Techniques | |||||
| Density g/cm3 | 3.07 | Crucible | Graphite | |||
| Melting Point °C | 1257 Sublimes | Coil | ||||
| E-Beam | Poor | Boat | Mo & W | |||
| Qty in grams: | Index of Refraction @ microns | 1.38 @ 0.55 | |||
| A1-5031-M SuperVac® Aluminium Nitride, AlN, 1-3mm pieces, 99.9% pure | Evaporation Techniques | |||||
| Density g/cm3 | 3.26 | Crucible | ||||
| Melting Point °C | Sublimes | Coil | ||||
| E-Beam | Fair | Boat | ||||
|  | Qty in grams: | Index of Refraction @ microns | |||
| A1-5015-M SuperVac® Aluminium Oxide, Al2O3, 3-12mm pieces (clear, single-crystal), 99.99% pure | Evaporation Techniques | |||||
| Density g/cm3 | 3.97 | Crucible | ||||
| Melting Point °C | 2045 | Coil | ||||
| E-Beam | Excellent | Boat | W | |||
| Qty in grams: | Index of Refraction @ microns | 1.59 @ 0.60, 1.56 @ 1.6 | |||
| A1-5016-M SuperVac® Aluminium Oxide, Al2O3, 3-12mm pieces (opaque, sintered), 99.8% pure | Evaporation Techniques | |||||
| Density g/cm3 | 3.97 | Crucible | ||||
| Melting Point °C | 2045 | Coil | ||||
| E-Beam | Excellent | Boat | W | |||
| Qty in grams: | Index of Refraction @ microns | 1.59 @ 0.60, 1.56 @ 1.6 | |||
| A1-5017-M SuperVac® Aluminium Oxide, Al2O3, 1-3mm pieces (clear, single-crystal), 99.99% pure | Evaporation Techniques | |||||
| Density g/cm3 | 3.97 | Crucible | ||||
| Melting Point °C | 2045 | Coil | ||||
| E-Beam | Excellent | Boat | W | |||
| Qty in grams: | Index of Refraction @ microns | 1.59 @ 0.60, 1.56 @ 1.6 | |||
| A1-5018-M SuperVac® Aluminium Oxide, Al2O3, 1-3mm pieces (opaque, sintered), 99.8% pure | Evaporation Techniques | |||||
| Density g/cm3 | 3.97 | Crucible | ||||
| Melting Point °C | 2045 | Coil | ||||
| E-Beam | Excellent | Boat | W | |||
| Qty in grams: | Index of Refraction @ microns | 1.59 @ 0.60, 1.56 @ 1.6 | |||
| A1-5024-M SuperVac® Aluminium Oxide, Al2O3, 10mm x 10mm white tablets, 99.99+% pure | Evaporation Techniques | |||||
| Density g/cm3 | 3.97 | Crucible | ||||
| Melting Point °C | 2045 | Coil | ||||
| E-Beam | Excellent | Boat | W | |||
| Qty in grams: | Index of Refraction @ microns | 1.59 @ 0.60, 1.56 @ 1.6 | |||
| A1-5032-M SuperVac® Aluminium Oxide, Al2O3, 2.5-5mm pieces, 99.99% pure | Evaporation Techniques | |||||
| Density g/cm3 | 3.97 | Crucible | ||||
| Melting Point °C | 2045 | Coil | ||||
| E-Beam | Excellent | Boat | W | |||
| Qty in grams: | Index of Refraction @ microns | 1.59 @ 0.60, 1.56 @ 1.6 | |||
| A1-5035-M SuperVac® Aluminium Oxide-Scandium Oxide, Al2O3-Sc2O3, 3-12mm pieces, 99.9% pure | Evaporation Techniques | |||||
| Density g/cm3 | 4.9 | Crucible | ||||
| Melting Point °C | 1700 | Coil | ||||
| E-Beam | Good | Boat | ||||
| Qty in grams: | Index of Refraction @ microns | n= 1.68 (500nm) | |||
| A1-5036-M SuperVac® Aluminium Oxide-Zirconium Oxide, Al2O3-ZrO2, 1-5mm pieces, 99.99% pure | Evaporation Techniques | |||||
| Density g/cm3 | Crucible | |||||
| Melting Point °C | Coil | |||||
| E-Beam | Boat | |||||
Qty in grams: | Index of Refraction @ microns | |||||
| A1-5037-M SuperVac® Aluminium Oxide-Titanium Dioxide, Al2O3-TiO2 90-10 wt%, 3-10mm pieces, 99.99% pure | Evaporation Techniques | |||||
| Density g/cm3 | Crucible | |||||
| Melting Point °C | Coil | |||||
| E-Beam | Good | Boat | ||||
| Qty in grams: | Index of Refraction @ microns | ||||
| A1-5019-M SuperVac® Aluminium Selenide, Al2Se3, 6mm pieces & smaller, 99.9% pure | Evaporation Techniques | |||||
| Density g/cm3 | Crucible | |||||
| Melting Point °C | Coil | |||||
| E-Beam | Boat | |||||
 | Qty in grams: | Index of Refraction @ microns | ||||
| A1-5022-M SuperVac® Aluminium Telluride, Al2Te3, 6mm pieces & smaller, 99.9% pure | Evaporation Techniques | |||||
| Density g/cm3 | Crucible | |||||
| Melting Point °C | Coil | |||||
| E-Beam | Boat | |||||
| Qty in grams: | Index of Refraction @ microns | ||||
| A1-5023-M SuperVac® Aluminium Telluride, Al2Te3, 6mm pieces & smaller, 99.999% pure | Evaporation Techniques | |||||
| Density g/cm3 | Crucible | |||||
| Melting Point °C | Coil | |||||
| E-Beam | Boat | |||||
| Qty in grams: | Index of Refraction @ microns | ||||